粉末冶金相关英语

多~

粉末冶金材料术语中英对照版
与材料有关的术语	烧结工艺
烧结材料sintered material	预烧presintering
烧结铁sintered iron	连续烧结continuous sintering
烧结钢sintered steel	间歇烧结batch sintering
重合金heavy metal	活化烧结activated sintering
弥散强化材料dispersion－strengthened material	加压烧结pressure sintering
金属陶瓷cermet	气压烧结gas pressure sintering
烧结金属基复合材料sintered metal－matrix composite MMC	松装粉末烧结loose－powder sintering
与应用有关的术语	反应烧结reaction sintering
烧结零件sintered part	液相烧结liquid－sintering
烧结结构零件sintered structural part	固相烧结solid－sintering
含油轴承oil-retaining bearing	过烧oversintering
烧结金属过滤器sintered metal filter	欠烧undersintering
烧结磁性零件sintered magnetic part	熔渗infiltration
烧结摩擦材料sintered friction material	粘结剂脱除binder removal
烧结电触头材料sintered electrical contact material	脱蜡dewaxing，burn－off
烧结后处理	快速烧除rapid burn－off
复压re-pressing	碳化carburizing
精整sizing	烧结sintering
整形coining	填料packing material
粉末锻造powder forging	吸气剂getter
烧结锻造sinter forging	造孔剂pore－forming material
热复压hot re-pressing	粘结相binder phase
浸渍impregnation	粘结金属binder metal
水蒸气处理steam treatment	压坯性能
烧结零件性能	生坯green
密度density	生坯密度green density
相对密度relative density	生坯强度green strength
实体密度solid density	棱边强度edge strength
密度分布density distribution	中立层neutral zone
径向压溃强度radial crushing strength	压制裂纹pressing crack
孔隙pore	分层lamination
开孔open pore	弹性后效spring back
闭孔closed pore	模具和接合器
空隙度porosity	模具mould
开孔空隙度open porosity	模架tool set
闭孔空隙度closed porosity	接合器adaptor
连通孔隙interconnected porosity	接合器台板adaptor table
扩散孔隙diffusing porosity	阴模die
孔隙结构porosity structure	阴模固定板die plate

多~

孔径 pore size 楔铁 wedge
孔径分布 pore size distribution 上模冲 upper punch
起泡压力 bubble－point pressure 模冲固定板 punch plate
: X( D. N( A9 F4 \$ W& d' a含油量 oil content 底板 base plate，lower coupler plate
流体透过性 fluid permeability 下模冲 lower punch
表观硬度 apparent hardness 模套 bolster
" b$ V7 S* ~; g! s" i# R实体硬度 solid hardness 压紧环 clamp ring
网状氧化物 oxide ['?ksaid] network 柱 column
表层指状氧化物 surface finger oxide 芯棒 core rod
烧结现象 拨叉 fork
烧结颈形成 neck formation 调节杆 lifting rod
起泡 blistering 装粉靴 feed shoe
发汗 sweating 上压头 upper ram
- G( [3 t3 d4 C8 Z$ c: V6 n胀大 growth 下压头 lower ram
收缩 shrinkage 模冲 punch
烧结壳 sinter skin 组合模冲segmented punch
烧结条件和烧结炉 脱模器 ejector
7 Z% g& D2 b6 i/ y6 k$ _烧结温度 sintering temperature 多模具接合器 multiple－tool adaptor
1 S5 y+ Q5 U+ b9 P3 D1 N烧结时间 sintering sintered time 倒锥 back relief
烧结气氛 sintering atmosphere 多工件模架 multiple－die se
M( A& {1 y6 X }- q8 `" f W6 ` y烧结炉 sintering furnace 浮动阴模 floating die
真空炉 vacuum furnace 可拆阴模 split die
连续炉 continuous furnace 复合阴模 sandwich die
间歇炉 batch furnace 拼合阴模 segmenged die
. v) t5 ^2 t2 {! T% n& e6 B网带炉mesh belt furnace 成形条件
2 Z9 w% d/ s3 o0 ?步进梁式炉 walking－beam furnace 装粉量 fill
推杆式炉 pusher furnace 容积装粉法 volume filling
" \ V. u, `; I" p6 b- x/ q' D粉末性能，测试方法，测试设备和测试结果 重量装粉法 weight filling
自然坡角度 angle of repose 振动装粉法 vibration－assisted filling
松装密度 apparent density 过量装粉法 overfill system
散装密度 bulk density 欠量装粉法 underfill system
7 o7 ?8 q, B' |9 o7 R j振实密度 tap density 装粉位置 fill position
压缩性 compressibility 装粉高度 fill height
5 Z& G8 i: R' D# ^成形性 compactibility 装粉体积 fill volume
' m2 {6 K% b% R. ? \: @1 P, P压缩比 compression ratio 压制压力 compacting pressure
' N+ a- I) N1 b+ O! N& r2 i装填系数 fill factor 保压时间 dwell time
5 U k5 P2 G6 N+ C9 A4 c流动性 flowability 脱模操作 ejection process
流动时间 flow time 拉下脱模法 withdrawal process
2 T3 n/ k* J- `$ G氢损 hydrogen loss 拉下位置 withdrawal position
氢可还原氧 hydrogen－reducible oxygen 平衡压力 counrer－pressure
离析 demixing，segregation 上模冲压紧压力 top－punch hold－down pressure
比表面积 specific surface area 粉末冶金压制工艺
分级 classification 冷压 cold pressing

多~

粒度 particle size 温压 warm pressing
# H% k) p' a9 T$ W5 ?. r粒度分布 particle size distribution 热压 hot pressing
/ f6 [/ _: D8 c- }1 [& z淘析 elutriation 单轴向压制 uniaxial pressing
粒度级 cut 单向压制 single－actio pressing
" m& _( O" ]" P$ ] c- t+ I筛分析 sieve analysis，screen analysis，screen classification 双向压制 double－action pressing
* P6 \4 `$ `2 g# Q沉降 sedimentation 多模压制 multiple pressing
取样器 sample thief 等静压制 isostatic pressing
8 x y( v! H8 E7 z! X% u分样器 sample splitter 冷等静压制 cold isostatic pressing
- d& d1 u7 a* g套筛 sieve set 温袋等静压制 wet－bag isostatic pressing
流速计 flowmeter 干袋等静压制 dry－bag isostatic pressing
) G4 Z2 u4 z% }& F振实密度仪 tapping appparatus 热等静压制 hot isostatic pressing
筛上物 oversize 装套 encapsulation
! h/ p) f; N3 U0 _. t$ j A筛下物 undersize 封装 canning
, v8 W% m$ I9 R# T0 [细粉 fines 金属粉末注射成形 metal powder injection moulding
筛上颗粒 oversize particle 粉末轧制 powder rolling
" E Y! d) n7 H$ l4 s2 z筛下颗粒 undersize particle 振动压制 vibration－assisted compaction
拱桥效应 bridfing 连续喷雾沉积 continuous－spray deposition
" u1 S0 X4 U# `* `成形 forming 修形 shaping
固结 consolidation 增塑粉末挤压 plasticized－powder extrusion
压制 pressing 粉末
压制成形 compacting 粉末 powder
3 A2 P' W. U! |压坯 compact，green compact 颗粒 particle
毛坯 blank 团粒 agglomerate
复合压坯 compound compact 粉浆 slurry
预成形坯 perform 粉块 cake
骨架 skeleton 坯料 feedstock
+ ], B* q1 R) R8 f0 E O粉末颗粒形状 粉末类型
颗粒形状 particle shape 雾化粉 atomized powder
针状 acicular 羰基粉 carbonyl powder
$ M1 C4 e# E, m角状 angular 粉碎粉 comminuted powder
1 ~0 \3 ?1 X1 I2 Y w树枝状 dendritic 电解粉 electrolytic powder
. h, b& I: A# {纤维状 fibrous 沉淀粉 precopitated powder
片状 flaky，flaked 还原粉 reduced powder
粒状 granular 海绵粉 sponge powder
& D! d. t5 j' o5 u' e' @9 W不规则状 irregular 合金粉 alloyed powder
瘤状 nodular 完全合金粉 completely alloyed powder
1 p8 [ P9 K+ F" r ~6 i4 e* o球状 spheroidal 预合金粉 pre－alloyed powder
粉末预处理 部分合金化粉 patically alloyed powder
合批 blending 扩散合金粉 diffusion alloyed powder
5 { C5 Q6 p6 W$ \6 _混合 mixing 机械合金化粉 mechanically alloyed powder
0 s4 E/ W6 i- ?1 n! L. v/ G1 p研磨 milling 母合金粉 master alloyed powder
制粒 granulation 复合粉 composite powder

多~

喷雾干燥 spray drying 包裹粉 coated powder
4 Y) b) M; S0 S, u' X7 p) r/ c: ?超生雾化 ultrasonic gas－atomizing 合批粉 blended powder
快速冷凝 chill－block cooling 混合粉 mixed powder
反应研磨 reaction milling 预混合粉 pre－mixed powder
! M: Z+ N( m2 X% q; L/ F3 D' V9 i1 d机械合金化 mechanical [mi'kænik?l] alloying ['æl?ii?]
/ r3 D6 u. G$ u! h; e% O氢化－脱氢粉 dehydride powder
其它 快速冷凝粉 rapidly solidfied powder
磨削 grinding 捣碎粉 chopped powder
0 m& v* n) ~( }* F5 _8 x, ]铣削 milling 超声震荡气化雾化粉 ultrasonically gas－atomized powder
8 G P; S( O% Q4 i7 t裂变 fission
摩擦 friction 粉末添加剂
机器 machine 仪器 instrument 设备 equipment 粘结剂 binder
加工面/作业面 founctional surface 掺杂剂 dopant
临近表面 adjacent surface 润滑剂 lubricant
, `* x' Y4 ~% d" G; b z! n# ?缺口 nick 增塑剂 plasticizer
+ c! @/ T2 X2 b刻痕，槽口 notch 增溶剂 solubilizer
裂纹，瑕疵 flaws 防锈剂 rust preventive
( z; J4 s, @4 ]/ M刮痕 scatch 清洗剂 cleaning agent
气泡 blow hole 光亮剂 lustre-coating agent
锐边 sharp edge 金相 metallography
1 y/ v* o }. q- s) M9 h毛刺 burr 去毛刺 burr removal / deburr
倒圆角 round
0 G1 X. l. ^" F3 i$ D/ P; m扩孔器，铰刀，铰孔 reamer 回火马氏体tempered martensite
粗加工 rough machining 网状碳化物carbide network
: b: U3 a0 E. G% q) @2 {& ?淬火harden 回火temper 电阻炉electric resistance furnace
保温时间 soaking time
0 R8 C6 ~! H1 O

粉末冶金名词解释
1、烧结sintering
% B; \, g; t& W/ r7 Y( d粉末或压坯在低于主要组分熔点的温度下的热处理，目的在于通过颗粒间的冶金结合以提高其强度。
2 f8 v! `' v+ e+ }* x! b3 f2、填料packing material
在预烧或烧结过程中为了起分隔和保护作用而将压坯埋入其中的一种材料。
! G W3 k: d% l% x, f( t3、预烧pre-sintering
在低于最终烧结温度的温度下对压坯的加热处理。
! ^; ?# v8 a/ Q4、加压烧结pressure
( f# H% A, ~7 A$ h在烧结同时施加单轴向压力的烧结工艺。
8 g! f9 m9 J W2 r0 t5、松装烧结loose-powder sintering，gravity sintering
粉末未经压制直接进行的烧结。
1 ]7 _7 j- m) ~6、液相烧结liquid-phase sintering
1 |$ _. l: Y0 @. D9 G至少具有两种组分的粉末或压坯在形成一种液相的状态下烧结。
7、过烧over sintering
; D, ~6 |, s; H; s" Z烧结温度过高和（或）烧结时间过长致使产品最终性能恶化的烧结。
) e% ?" r6 y6 A

多~

8、欠烧under sintering
- `. o! y8 l0 J: t! Y& _烧结温度过低和（或）烧结时间过短致使产品未达到所需性能的烧结。
9、熔渗infiltration
用熔点比制品熔点低的金属或合金在熔融状态下充填未烧结的或烧结的制品内的孔隙的工艺方法。
10、脱蜡dewaxing，burn-off
! N4 O* V& l" @% _# F用加热排出压坯中的有机添加剂（粘结剂或润滑剂）。
6 u+ |0 b* h8 N2 f) W11、网带炉meshbelt furnace
一般由马弗保护的网带将零件实现炉内连续输送的烧结炉。
12、步进梁式炉walking-beam furnace
5 Q* f2 Y4 V! Y: a& N: x6 | P通过步进梁系统将放置于烧结盘中的零件在炉内进行传送的烧结炉。
13、推杆式炉pusher furnace
" {& A* p W: R/ z) @( h' R2 l0 U* r将零件装入烧舟中，通过推进系统将零件在炉内进行传送的烧结炉。
2 K! b2 ^( v# A14、烧结颈形成neck formation
3 n2 W' C O( r' u2 c烧结时在颗粒间形成颈状的联结。
R* P) a! h9 t- R15、起泡blistering
由于气体剧烈排出，在烧结件表面形成鼓泡的现象。
2 u+ ~0 {, m u. g16、发汗sweating
! ]' v: v6 C( \4 P* B! i$ l压坯加热处理时液相渗出的现象。
, p" d4 X. d1 g3 m17、烧结壳sinter skin
0 l1 ~6 |' W. v8 Q, h8 J; i烧结时，烧结件上形成的一种表面层，其性能不同于产品内部。
18、相对密度relative density
多孔体的密度与无孔状态下同一成分材料的密度之比，以百分率表示。
1 N2 r! @* `' K5 O* V M( j6 [19、径向压溃密度radial crushing strength
通过施加径向压力测定的烧结圆筒试样的破裂强度。
20、孔隙度porosity
多孔体中所有孔隙的体积与总体积之比。
* t! u) r/ E7 R& Q4 K" J/ r. Y21、扩散孔隙diffusion porosity
9 |, \# }! `9 |: n由于柯肯达尔效应导致的一种组元物质扩散到另一组元中形成的孔隙。
22、孔径分布poresize distribution
# L8 I% _% E( R( y0 y材料中存在的各级孔径按数量或体积计算的百分率。
23、表观硬度apparent hardness
在规定条件下测定的烧结材料的硬度，它包括了孔隙的影响。
2 Y, Q4 o$ |7 y! X3 @) H) G' ~: l24、实体硬度solid hardness
) i6 l4 n( B; c8 Y" D% k在规定条件下测定的烧结材料的某一相或颗粒或某一区域的硬度，它排除了孔隙的影响。
25、起泡压力bubble-point pressure
6 j* J4 N9 F& A% [迫使气体通过液体浸渍的制品产生第一气泡所需的最小的压力。
26、流体透过性fluid permeability
- S5 [* R. u& n) ?3 p: v在规定条件下测定的在单位时间内液体或气体通过多孔体的数量。
5 ]# K" t3 S# {. w2 E, g6 O
: L9 [! R% ]/ d( c8 @' A