水里的云 发表于 2008-5-24 00:42:36

美国牌号“AISI O6”，找了很久没能找到国内材料代替---求助

现有客户需要我们公司加工产品，可是材料是美国牌号“AISI O6”，找了很久没能找到国内材料代替，请问各位大侠，有谁知道什么材料能够代替吗？谢谢了……
Searchfor    HomeMembershipPalm StoreForumSearch MemberCalculatorshttp://www.efunda.com/images/llc1.gifhttp://www.efunda.com/images/title4.gif
Materialshttp://www.efunda.com/images/mid_peg1.gifhttp://www.efunda.com/images/title3.gif
Designhttp://www.efunda.com/images/mid_peg1.gifhttp://www.efunda.com/images/title2.gif
Processeshttp://www.efunda.com/images/mid_peg1.gifhttp://www.efunda.com/images/title5.gif
Unitshttp://www.efunda.com/images/mid_peg1.gifhttp://www.efunda.com/images/title6.gif
Formulashttp://www.efunda.com/images/mid_peg1.gifhttp://www.efunda.com/images/title1.gif
Mathhttp://www.efunda.com/images/lrc1.gifhttp://www.efunda.com/images/4jobs_search.gif
AISI O6http://www.efunda.com/images/section_bar.gifCategory SteelClass Tool steelType Oil-hardening cold work steelDesignations United States: ASTM A681 , FED QQ-T-570 , SAE J437 , SAE J438 , UNS T31506 Compositionhttp://www.efunda.com/images/section_bar.gifElement Weight % C 1.25-1.55 Mn 0.30-1.10 Si 0.55-1.50 Cr 0.30 Ni 0.30 Mo 0.20-0.30 Cu 0.25 P 0.03 S 0.03

水里的云 发表于 2008-5-27 08:42:58

目前国内好像找不到合适的材料能够代替，郁闷

cs-baby 发表于 2008-5-28 07:58:08

应该是AISI 1006吧?
LZ再确认下,
1006的话替代材为08F

水里的云 发表于 2008-5-28 13:39:35

感谢楼上的，我们最初也是认为是08F，可是后来我们与客户确认后还是应该为O6（注：不是06），客户也提供了O6的化学成分，如上面的图，我们实在是找不到合适的材料代替啊，O6是油淬冷作工具钢。

三脚猫 发表于 2008-5-28 14:28:49

美国AISI/SAE标准和UNS系统合金工具钢
油淬冷作工具钢
AISI/SAE--06、UNS--T31506
C 1.35-1.55、Si 0.80-1.20、Mn 0.30-1.00、Mo 0.20-0.30

只查到
中   国               美    国
9Mn2V          02   T31502
CrWMn         07
9CrWMn            T31501
MnCrWV       01
9Mn2            02

替代材料一般是从两方面着手
1、化学元素接近
2、机械性能相似
建议楼主从机械性能方面着手

http://www.eanshan.com/steellore/652.asp

[ 本帖最后由 三脚猫 于 2008-5-28 15:06 编辑 ]